In Vitro Effects of Different Surface Preparation Techniques on Shear Bond Strength of Direct to Indirect Composite Resin
A Kaviani, N Gharizadeh, H Alinejad *, R Moosavi
Postgraduate Student Dept. of Operative Dentistry , hengamehalinejad@yahoo.com
Abstract:   (2732 Views)

  Objective: Repair of an indirect restoration is usually preferred over its replacement. This study aimed to evaluate the effect of silane in different surface preparation techniques on the bond strength of direct to indirect composite resin.

  Methods: For this in vitro experimental study, 48 indirect composite cubes were fabricated, divided into 4 groups of 12 and subjected to the following preparation techniques: Group 1. Sandblasting with 50μaluminum oxide particles (SB), Group 2. Sandblasting+ silanization (SB+Sil), Group 3. Etching with 9.5% hydrofluoric (HF) acid, Group 4. Etching with 9.5% HF acid+ silanization (HF+Sil). Before the restoration process, specimens were subjected to 500 thermal cycles and received surface preparations. Single Bond adhesive was applied to the surface in all groups. Specimens were restored with direct composite resin and stored in an incubator at 37°C for 24h. Fracture was induced in the specimens by an Instron machine and the shear bond strength was measured. Data were converted to mega Pascal and analyzed using two-way ANOVA and Tukey’s post hoc.

  Results: The highest shear bond strength was 13.85 (2.75) MPa and belonged to group 1 while the lowest bond strength was 8.43 (1.35) MPa and observed in group 2.

  Conclusion: Based on the obtained results, composite surface preparation by sandblasting yields more favorable results than HF acid etching and application of silane can also increase the bond strength.

Keywords: Dentin bonding agents, Shear bond strength, Silane, Stress, Surface preparation.
Full-Text [PDF 391 kb]   (407 Downloads)    
Type of Study: Original Article | Subject: Special
Received: 2014/04/22 | Accepted: 2014/04/22 | Published: 2014/04/22
Send email to the article author

Add your comments about this article
Your username or email:

Write the security code in the box >



XML     Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Kaviani A, Gharizadeh N, Alinejad H, Moosavi R. In Vitro Effects of Different Surface Preparation Techniques on Shear Bond Strength of Direct to Indirect Composite Resin. J Dent Sch. 2014; 32 (2) :96-102
URL: http://jds.sbmu.ac.ir/article-1-1242-en.html
Volume 32, Number 2 (Spring 2014) Back to browse issues page
مجله دانشکده دندانپزشکی دانشگاه علوم پزشکی شهید بهشتی Shahid Beheshti University Dental Journal
Persian site map - English site map - Created in 0.048 seconds with 798 queries by yektaweb 3506