The Effect of Different Coating Methods on Resin Bond Strength to Zirconia
Dr. Maryam Moezzyzadeh, Dr. Hanieh Nojehdehyan, Corresponding Author: Dr. Haleh Valizadeh Haghi *
Postgraduate Student Dept. of Operative Dentistry , hvh_haleh@sbmu.ac.ir
Abstract:   (2242 Views)

Objective: A clinical challenge of using zirconia frameworks is to achieve adequate bond with different substrates. This study aimed to evaluate the effect of bioglass and silica coating of zirconia substrates on microshear bond strength of resin cement to tetragonal zirconia. Methods: This laboratory experimental study was conducted on zirconia discs. A total of 120 YTZP zirconia (Zirkonzahn) discs were fabricated and based on surface treatments were categorized into 8 groups of 15 including 1. Control, 2.Sandblast, 3. Etch + bioglass powder coating, 4. Silane + etch + bioglass powder coating, 5. Etch + bioglass slurry coating, 6. Silane + etch+ bioglass slurry coating. 7. Silane + colloidal silica coating, and 8. Silane + etch + colloidal silica coating. Samples were subjected to microshear bond strength testing. In coated groups, thickness of the coating was measured as well. Kruskal Wallis test and ANOVA were applied for intragroup statistical analysis and Dunnett’s test and Mann Whitney U test were used for pairwise comparisons.

Results: The mean bond strength of silica-coated samples was significantly lower than the sandblasted specimens (P<0.001). No significant difference was detected in the mean bond strength between specimens with different glass coatings and sandblasted samples. In other words, bond strength of sandblasted and different glass-coated samples was not significantly different. The thickness of coating in the slurry group was significantly less than in other groups.

Conclusion: Bioglass coating could effectively increase the bond strength of resin cement to zirconia in short-term.

Keywords: Tetragonal zirconia, Resin cement, Microshear bond strength.
Full-Text [PDF 115 kb]   (1054 Downloads)    
Type of Study: Original Article | Subject: Special
Received: 2013/07/21 | Accepted: 2013/10/12 | Published: 2013/10/12
Send email to the article author

Add your comments about this article
Your username or email:

Write the security code in the box >



XML     Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Moezzyzadeh M, Nojehdehyan H, Valizadeh Haghi H. The Effect of Different Coating Methods on Resin Bond Strength to Zirconia . J Dent Sch. 2013; 31 (2) :95-103
URL: http://jds.sbmu.ac.ir/article-1-1133-en.html
Volume 31, Number 2 (Spring 2013) Back to browse issues page
مجله دانشکده دندانپزشکی دانشگاه علوم پزشکی شهید بهشتی Shahid Beheshti University Dental Journal
Persian site map - English site map - Created in 0.047 seconds with 795 queries by yektaweb 3506